Influence of Simulated LOCA on the Properties of Zircaloy Oxide Layers
DOI:
https://doi.org/10.14311/1067Keywords:
Zirconium alloys, oxide layers, semiconductor doping conduction type, reduction semiconductor, anomalous I-V characteristics, space-charge limited currents, injection and extraction currents, temperature dependence of resistivity, activation energyAbstract
Specimens of Zr1Nb and Zry-4W were pre-oxidized first for 360 days in steam at 425 °C and were then exposed for 3 min to 1200 °C in steam, simulating loss of coolant conditions. In this way, the oxide thickness was more than doubled. The I-V characteristics, measured up to 90 V at temperatures up to 180 °C, revealed the formation of double layers, consisting of dark monoclinic oxide with 1.3 eV activation energy near the metal, and of a whitish surface phase with only 0.5 eV, for both samples. The I-V characteristics of Zr1Nb showed normal behavior, whereas Zry-4W changed from an unusual sub-linear form at low temperatures and voltages to normal space-charge limited currents at higher temperatures and voltages. Observation of the injection and extraction currents in the Zry-4W sample showed abnormally high negative zero voltages produced by extraction after former injection.Downloads
Downloads
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
4. ddd